Search for: [Description = This article deals with the optimization of friction stir welding process parameters with filler ratios on dissimilar Aluminium alloy groups. For this purpose, 6 series Aluminium alloy 6082 and 5 series Aluminium alloy 5052 were taken. Microhardness property was conducted under various rotational speeds, welding speed, plunge depth, Center distance between the holes and filler mixing ratio. The Central Composite Design \(CCD\), the most commonly used Response Surface Methodology \(RSM\), is considered to develop the prediction equation. A validation analysis is carried out, and the results were compared with the relative impact of input parameters on weld nugget microhardness. It is observed that the increase in welding speed with plunge depth and filler ratio result in the increase of weld nugget microhardness up to a maximum value. The maximum weld nugget hardness of fabricated joint was obtained with the welding process parameters combination of 1000 rpm rotational speed, 125 mm\/min welding speed, 0.15 mm plunge depth, 2 mm centre distance between the holes, and filler ratio of 95% Mg and 5% Cr.]

Number of results: 1