Tytuł: Evaluation of physical and dynamic mechanical properties of coconut husk ash (CHA) reinforced polyester composites

Opis:

The evaluation of physical and dynamic mechanical analysis (DMA) properties was carried out using developed CHA Reinforced Polymer Composite. Sieve analysis of pretreated CHA was done to obtain 75 µm, 150 µm and 300 µm particles sizes. These particles were used at varying compositions of 5%, 10%, 15%, 20% and 25% as reinforcements for polyester composites. The catalyst and accelerator used were Methyl Ethyl Ketone Peroxide and Cobalt Naphthenate respectively. The densities of the evaluated composites made with 150 μm particles were found to be less dense with values ranging from 0.9792 g/cm3 to 1.2561 g/cm3 than those made with 75μm and 300μm. The results also show that the percentage water absorbed by samples increased, ranging from 0 to over 2000 E’/MPa for all percentage reinforcements of CHA, with an increase in the duration of immersion of the samples in distilled water. However, 25% reinforcement had better results for all particle sizes. There were obvious variations of storage modulus, loss modulus and mechanical loss factor with percentage weight of reinforcement, temperature and frequency. The composite with 15 % reinforcement displayed better results and can be used as a material for interior components in aerospace and automobile industries.

Miejsce wydania:

Koszalin

Wydawca:

Publishing House of the Koszalin University of Technology

Format:

application/pdf

Identyfikator:

oai:dlibra.tu.koszalin.pl:1511

Język:

eng

Jest częścią:

Journal of Mechanical and Energy Engineering. Vol.4 (44), nr 4, s. 315-324

Prawa:

Biblioteka Politechniki Koszalińskiej

Prawa dostępu:

internet

Licencja:

Creative Commons BY 4.0

Kolekcje, do których przypisany jest obiekt:

Data ostatniej modyfikacji:

6 lis 2023

Data dodania obiektu:

17 cze 2022

Liczba wyświetleń treści obiektu:

19

Wszystkie dostępne wersje tego obiektu:

https://dlibra.tu.koszalin.pl/publication/1515

Wyświetl opis w formacie RDF:

RDF

Wyświetl opis w formacie OAI-PMH:

OAI-PMH

×

Cytowanie

Styl cytowania:

Ta strona wykorzystuje pliki 'cookies'. Więcej informacji